Material: Grado del PE: Precio de la película: Muestra del precio de fábrica: Tiempo de entrega gratis: Dentro de 12 días Fábrica: Visita Paquete del transporte: 25kg Bolsas de los PP Origen: China Color: Borrar Natural / Blck / Rojo / Azul Inspección: SGS MOQ: 5 toneladas Materiales: Gránulo de materia prima plástico Nuestras existencias: LDPE / HDPE / LLDPE / PP Marca registrada: ns Especificación: grado pp Código HS: 3901100090 Dow Sabic marca resina de plástico virgen HDPE y sol; LDPE y sol; LLDPE

em	Test data	comments
proportion g/cm3	0.959	ISO  1183
melt flow rate(190°C/5.0kg)g/10min	0.22	ISO  1133
Carbon black dispersion	≤ 3	ISO  18553
Carbon black content	≥ 2.0%	ASTM D-1603
tensile modulus MPa	1100	ISO 527-2/1
tensile stress (yield) MPa	25.0	ISO 527-2/50
tensile strain(breakage)	>600%	ISO 527-2
Resistance to slow crack growth 3(80°C)	>1000hr	ISO 13479
Resistance to rapid crack propagation	> 10.0bar	ISO 13477
Oxygen induction time	> 20min

Item	Unit	Test Standard	Value
Melt flow rate	g/10min	ISO 1133	12
Tensile modulus of elasticity(v=1mm/min)	Mpa	ISO 527-2	1550
Tensile yield at stress(v=50mm/min)	Mpa	ISO 527-2	35
Tensile yield at strain (v=50mm/min)	%	ISO 527-2	8
Tensile strain at break (v=50mm/min)	%	ISO 527-2	>50
Charpy impact strength unnotched(+23°C)	kJ/m2	ISO 179/1eU	110
Charpy impact strength notched(+23°C)	kJ/m2	ISO 179/1eA	3.0
Izod Impact strength notenched(+23°C)	kJ/m2	ISO 180/1A	3
Ball indentation hardness(H 358/30)	Mpa	ISO 2039-1	78
Melting point,DSC	°C	ISO 3146	163
Heat deflection temperature (0.45Mpa)	°C	ISO 75-2	85
Vicat softening temperature  VST/A50(10N)	°C	ISO 306	154
Density	g/cm3	ISO 1183	0.91

Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C

Moldeo por soplado Grado HDPE

Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%

Grupos de Producto : Resina plástica > Otros Resina Plástica